VESTOLIT P 1430 K90 Ultra
Polyvinyl chloride for paste processing
VESTOLIT P 1430 K90 Ultra is a paste-forming homopolymer which is suitable for producing low viscosity pastes with almost Newtonian flow and good storage stability.
This product was developed for low-plasticiser content pastes e.g. mat, transparent top coats, which are particularly suitable for use in CV floor covering top coats.
The advantage of VESTOLIT P 1430 K90 Ultra is its low viscosity and excellent de-aeration properties. The superb transparency, mat surface finish and good mechanical properties in gelled films are tailored especially to to meet the demands of top coats in CV flooring. VESTOLIT P 1430 K90 Ultra can be easily stabilized using both Ca/Zn and Sn stabilizers.
| Aplication | Solid | Foam |
|---|---|---|
| Coated fabrics |
○ |
|
| Floor coverings |
● |
|
| Wallpapers, wall coverings |
|
|
| Canvas coating |
○ |
|
| Unsupported layers, films |
|
|
| Dipping, casting |
○ |
|
| Spray coating |
|
|
● recommended ○ feasible
| Property | Method | Unit | Value * |
|---|---|---|---|
| K value |
DIN EN ISO 1628-2 |
- |
90 |
| Viscosity number |
DIN EN ISO 1628-2 |
cm3/g |
227 |
| Apparent bulk density |
DIN EN ISO 60 |
g/cm3 |
0,35 |
| Sieve analysis - retained on 0.063 mm sieve |
DIN EN ISO 1624 |
% |
< 1 |
| Water content according to K. Fischer |
DIN 53 715 |
% |
≤ 0,3 |
| pH value of the aqueous extract |
DIN EN ISO 1264 |
- |
6 |
| Paste viscosity 1.5 /s |
|
Pa s |
1,6 |
| Paste viscosity 45 /s |
|
Pa s |
2,0 |
* The figures quoted above are typical values, and do not form part of the specification. 100 parts PVC, 60 parts DINP - measured in a rotary viscometer with a defined shear gap at 25 °C after ageing for 2 hours.
Contact
VESTOLIT GmbH
Paul-Baumann-Str. 1
45772 Marl
Germany
T. +49 2365 9549-888
F. +49 2365 9549-4000
products.vinyl.eu@mexichem.com
Data Sheet
VESTOLIT GmbH
Mexichem Business Group Vinyl