Polyvinyl chloride for paste processing
VESTOLIT P 1430 K70 Ultra is a paste-forming homopolymer which is suitable for producing low viscosity pastes with almost Newtonian flow.
VESTOLIT P 1430 K70 Ultra is particularly suited to the production of compact pastes.
VESTOLIT P 1430 K70 Ultra has very good de-aeration properties. P 1430 K70 Ultra produces finished articles with good transparency, high gloss and very good thermostability. These properties, combined with its low viscosity make it very suitable for the production of tarpaulins and transparent wear layers with high gloss for floorings.
Application | Solid | Foam |
---|---|---|
Coated fabrics |
○ |
|
Floor coverings |
● |
|
Wallpapers, wall coverings |
|
|
Canvas coating |
● |
|
Unsupported layers, films |
● |
|
Dipping, casting |
● |
|
Spray coating |
○ |
|
● recommended ○ feasible
Property | Method | Unit | Value * |
---|---|---|---|
K value |
DIN EN ISO 1628-2 |
- |
70 |
Viscosity number |
DIN EN ISO 1628-2 |
cm3/g |
125 |
Apparent bulk density |
DIN EN ISO 60 |
g/cm3 |
0,35 |
Sieve analysis - retained on 0.063 mm sieve |
DIN EN ISO 1624 |
% |
< 1 |
Water content according to K. Fischer |
DIN 53 715 |
% |
≤ 0,3 |
pH value of the aqueous extract |
DIN EN ISO 1264 |
- |
6 |
Paste viscosity 1.5 /s |
|
Pa s |
1,7 |
Paste viscosity 45 /s |
|
Pa s |
2,1 |
* The figures quoted above are typical values, and do not form part of the specification. 100 parts PVC, 60 parts DINP - measured in a rotary viscometer with a defined shear gap at 25 °C after ageing for 2 hours.